Products

Mukesh Steel is included in Manufacturing and Exporting of astounding stainless steel 410 sheets, stainless steel 410 plates, stainless steel 410 loops in thickness of 0.3mm to 120mm. that have discovered broad applications in different commercial ventures. We likewise bargain in Nickel and copper amalgam, Stainless and Duplex Steel, Carbon and Alloy Steel, are the materials which are utilized for planning of stainless steel sheet, plate and coil.

Alloy 410 is utilized as a part of numerous applications and additionally numerous commercial enterprises. In the oil business, 410 stainless Steel plate is utilized to make solidified steel balls, seats, spouts, and valve parts in oil well pumps, and, in the paper and mash industry, is utilized to make isolating screens and strainers. 410 stainless Steel plate is additionally utilized as a part of the restorative business for the manufacture of surgical and dental instruments.

Stainless Steel 410 Sheet Sizes

Steel grades	AISI410 (1.4000)
Production	Cold-rolled
Standard	ASTM A240/A480
Thickness	Min: 0.4mm Max: 6.0mm
Width	1000mm, 1250mm, 1500mm, 2000mm, Other sizes on request
Finish	2B, BA, MATT, M.PVC, N4, N5, SB, HR, N8, Oil base wet polished, Both sides polished available
Coating	PVC coating normal/laser Film: 100 micrometer Color: black/white
Package weight	1.0-2.2 tonnes
Application	Medical equipment, Food industry, Construction material, Kitchen utensils, BBQ grill, Building construction, Electric equipment,

Stainless Steel 410 Coil Sizes

Steel grades	AISI410 (1.4000)
Production	Cold-rolled, Hot-rolled
Standard	ASTM A240/A480
Thickness	Min: 0.4mm Max: 10.0mm
Width	1000mm, 1250mm, 1500mm, 2000mm, Other sizes on request
Finish	1D, 2B, BA, N4, N5, SB, HL, N8,Oil base wet polished, Both sides polished available
Coating	PVC coating normal/laser Film: 100 micrometer Color: black/white
Package weight (cold-rolled)	1.0-10.0 tonnes
Package weight (hot-rolled)	Thickness 3-6mm: 2.0-10.0 tonnes Thickness 8-10mm: 5.0-10.0 tonnes
Application	Medical equipment, Food industry, Construction material, Kitchen utensils, BBQ grill, Building construction, Electric equipment,

Stainless Steel 410 Plates Sizes

Steel grades	AISI410 (1.4000)
Production	Hot-rolled
Standard	ASTM A240/A480
Thickness	Standard: 3.0mm-30.0mm Over 30.0mm on request
Width	1000mm, 1250mm, 1500mm, 2000mm, Other sizes on request
Package weight	1.0-4.0 tonnes
Application	Medical equipment, Food industry, Construction material, Kitchen utensils, BBQ grill, Building construction, Electric equipment,

Chemical Composition

Grade		C	Mn	Si	P	S	Cr	Mo	Ni
410	Min	-	-	-	-	-	11.5	-	-
410	max.	0.08	2.0	0.75	0.045	0.030	20.0	10.5	0.10

Mechanical Properties

Tempering Temperature (0C)	Tensile Strength (MPa)	Yield Strength 0.2% Proof (MPa)	Elongation (% in 50mm)	Hardness Brinell (HB)	Impact Charpy V (J)
Annealed *	480 min	275 min	16 min	-	-
204	1310	1000	16	388	30
316	1240	960	14	325	36
427	1405	950	16	401	#
538	985	730	16	321	#
593	870	675	20	255	39
650	755	575	23	225	80
* Annealed properties are specified for Condition A of ASTM A276, for cold finished bar. # Due to associated low impact resistance this steel should not be tempered in the range 425-6000C

Physical Properties

Grade	Density (kg/m3)	Elastic Modulus (GPa)	Mean Coefficient of thermal Expansion (m/m/0C)			thermal Conductivity (W/m.K)		Specific Heat 0-1000C (J/kg.K)	Electrical Resistivity (n.m)
Grade	Density (kg/m3)	Elastic Modulus (GPa)	0-1000C	0-3150C	0-5380C	at 1000C	at 5000C	Specific Heat 0-1000C (J/kg.K)	Electrical Resistivity (n.m)
410	7750	200	9.9	11.4	11.6	24.9	28.7	460	570