Stainless steel 310 round bar manufacturer and exporter

310 stainless steel bar, otherwise called UNS S31000 and Grade 310, contains the accompanying essential components: .25% most extreme carbon, 2% greatest manganese, 1.5% greatest silicon, 24% to 26% chromium, 19% to 22% nickel, hints of sulfur and phosphorus, with the equalization being iron. Sort 310 is better in many situations than 304 or 309 because of its moderately high chromium and nickel content. It displays a mix of good quality and erosion resistance in temperatures up to 2100° F. Cool working will make 309 expansion in hardness and quality, and it doesn't react to warmth treatment.

310 Stainless Steel is an austenitic stainless steel. 310 consolidates great weldability and malleability with awesome high temperature properties. Containing a high substance of Nickel and Chromium 310 has great consumption resistance, fantastic imperviousness to oxidation and quality up to 2100°F. The higher Chromium and Nickel make this a better stainless steel when thought about than 304 or 309.

310 stainless steel comes in the accompanying shapes: round bar, channel, sheet, plate, tubing and curl

Standard	SS 310
UNS	S31000
WERKSTOFF NR.	1.4841
JIS	SUS 310

Specification

Standard	310 / 1.4841
Range	3.17mm to 350mm dia
Designation	ASTM A276, ASME SA276
Finish	Bright, Black, Polish, Export Bright
Thickness	4.0mm - 100mm
Type	Bar, Bright Bar, Black Bars, Hex Bar, Square Bar, Rods, Polish Bar, Forged Bar, Round Bar
Length	Random, Fix & Cut Length

Chemical Composition

Grade	C	Mn	Si	P	S	Cr	Mo	Ni	N
310	0.25 max	2 max	1.50 max	0.045 max	0.03 max	24 – 26	-	19 – 22	-

Mechanical Properties

Density	8.0 g/cm3
Melting Point	1454 °C (2650 °F)
Tensile Strength	Psi – 75000 , MPa – 515
Yield Strength (0.2%Offset)	Psi – 30000 , MPa – 205
Elongation	35 %

TYPES OF STAINLESS STEEL 310 ROUND BARS & RODS